分类: | E308LT1-1, SFA/AWS A5.22, Weld Metal, E308LT1-4, SFA/AWS A5.22, Weld Metal, YF 308LC, JIS Z 3323, Weld Metal, YF 308LC, KS D 3612, Weld Metal, T 19 9 L P C1 2, EN ISO 17633-A, Weld Metal, T 19 9 L P M21 2, EN ISO 17633-A, Weld Metal |
认证: | E308LT1-4 (M21), ABS, 308L (C1), BV, SA 308L (M21), BV, 308L (C1), CCS, EN 13479, CE, KW308LG(C), ClassNK, E308LT1-1 (C1), CWB, E308LT1-4 (M21), CWB, NV 308L (C1), DNV, VL 308L (M21), DNV-GL, RW308LG (C) (C1), KR, 304L (C1), LR, 04832 (M20,M21), VdTÜV |
Approvals are based on factory location. Please contact ESAB for more information.
Alloy Type: | C Cr Ni |
Welding Current: | DC+ |
焊缝金属分析
夏比V型缺口冲击性能
C1 Shielding gas As welded |
Impact Value | Testing Temperature |
60 J | -29 °C |
30 J | -196 °C |
Typical Tensile Properties
C1 Shielding gas As welded |
Elongation | Tensile Strength | Yield Strength |
45 % | 570 MPa | 380 MPa |
熔敷数据
安培 | 熔敷率 | 电压 V | 直径 | 送丝速度 |
130-220 A | 1.9-4.6 kg/h | 24-29 V | 1.2 mm | 5.8-14.4 m/min
|